Self Drying High Hardness Transparency Nano Silicon Floor Coatings
Product Introduction
WQ-0132 uses special nanotechnology to synthesize nano protective
coatings with excellent hardness, dirt resistance, high temperature
resistance, wear resistance and skid resistance by spraying,
rolling coating and rubbing. The particle size of WQ-0132 is about
30-50nm, which can produce chemical bond with the surface of
substrate, which makes it have excellent permeability and adhesion.
It can achieve long-term waterproof, oil-proof, acid-base
resistant, dirt proof, moisture-proof, cloud proof, chemical
resistance and self-cleaning.
WQ-WL0132 is a high hardness nano silicon paint cured at normal
temperature produced from the raw materials imported from Japan.Due
to high density 0-Si-O structures in its main chains,this product
is coated on the base material by spraying,dip-coating,roller
coating,etc,aked or dried at normal temperature and cured to obtain
a film with good physical properties,such as high hardness,high
transparency,good insulativity,and good chemical properties,such as
good high low temperature resistance,rub resistance,oxidation
resistance,radiation resistance,corrosion resistance,low
temperature not tendering,water repellent,anti-moisture,demoulding
and ventilating,non-toxic,chemical resistance,etc.
Composition
| Conc. wt.% | Ingredient | CAS NO. |
| 8-10% | silica | 7631-86-9 |
| 12%-13% | Siloxane | 1185-55-3 |
| 15%-18% | Organosilicone resin | 67763-03-5 |
| 35%-40% | Propylene glycol monoethylether | 1569-02-4 |
| 10%-15% | Butyl acetate | 123-86-4 |
Additional Isopropyl alcohol may be formed by reaction with
moisture.
Features:
1. Very high hardness,7H-9H,excellent resistance to
solvents,including alcohol,ketone,and esters.
2. High self-crosslinking density,similar to nano structures,super
strong water proof and fire proof performance,salt fog
resistance,mouldproof,anti-microbial,impermeability,ultraviolet
resistance,etc.
3. Resistance to 20% concentrated sulphuric acid and concentrated
hydrochloric acid,10%caustic soda,and strong polar solvents.
4. Very low surface tension,hydrophobic,high self-cleaning and
soiling resistance(water contact angle of resin surface:80°).
5. Good temperature resistance,between-40℃and 250℃,resistance to
cigarette end burn,instant high temperature resistance of about
600℃,excellent electrical insulating properties,air drying,one
component cross-linked curing,and strong adhesion.
6. Good chemical resistance,soiling resistance,resin hardness,and
weather resistance
Applications:
1. All floors: Concrete, stone, tile, epoxy, PU, PVC, log floor and
terrazzo/ground floor / tile / Stone / polyurethane / Wood /acrylic
/ UV paint / metal.
2. This product is suitable for surface glossy overprint and
protection of all kinds of top grade products,especially painting
on coating the polar colored coating surfaces,it can be used as an
additive in all kinds of paints and coatings,such as baking
varnish/UV/thermoplastic hydroxy acrylic air-dry paint,etc.
This product can be applied by roller coating,brush coating and
spraying.
Basic Functions
Test ltems | Test Results | Test Method |
|---|
| Pencil Hardness (Gouge Hardness) | 7H | CNS 10757(1995) |
| Taber Abrasion (g)(Wheel: CS-10; Load: 1000g, 500 cycles) | 0.007 | CNS 10757(1995) |
| Wash ability-(Steel Wool#0000)load 1kg,Area 1*1cm, 800 cycles) | 800 times | CNS 10757(1995} |
| Friction Test | Dry: Over 1.0
Wet: Over 0.9 | ASTMD1894-14 |
| Heat Resistance (300°C 1 hour) | No Cracks, No Peeling | CNS 10757(1995) |
| Resistance to Boiling Water (3 hrs.) | No Effect | CNS 10757(1995) |
| Stain Resistance (Black Tea, Coffee, Crayon, Lipstick, Marker Pen) | No Effect | CNS 10757(1995) |
| Solvent Wipe Test (MEK/IPA/Toluene, 1000 times) | No Effect | ASTMD4752-03 |
| Non-toxic Test (Eight Heave Metals) | No Detected | CNS 4797-2 |
| Permeable (Oil) | Less 0.2 | CNS10757 |
| Permeable (Pure Water) | Less 0.4 | CNS10757 |
| Chemical Resistance (Saturation NACL, Room temp. 1000 hrs.) | No Effect | CNS 10757(1995) |
| Chemical Resistance (MEK/Toluene/IPA, Room Temp. 1000 hrs.) | No Effect | CNS 10757(1995) |
| Acid Resistance (30%H2S04, Room Temp. 500 hrs.) | No Effect | CNS 10757(1995) |
| Alkali Resistance (20%NAOH, Room Temp. 500 hrs.) | No Effect | CNS 10757(1995) |
.
Packaging and Storage
packing:25kg/barrel
It should be placed in a cool and ventilated place with a shelf
life of 1 year