Water And Rub Resistance Soft Film Forming Acrylic Emulsion For Printing Ink

Product Categories

Water Based Acrylic Resin [180]
Solid Acrylic Resin [143]
Water Based Polyester Resin [21]
Polyethylene Wax Emulsion [82]
Water Based Alkyd Resin [31]
Solvent Based Acrylic Resin [60]
Water Based Epoxy Resin [44]
Mirror Effect Ink [46]
Epoxy Curing Agent [10]
Water Based Hydroxyl Acrylic Resin [36]
Water Based Peelable Resin [50]
High Hardness Floor Coatings [17]
Resins For Wood Coatings [27]
Water Based Industrial Coating Resins [29]

Xiamen WangQin Chemical Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Water And Rub Resistance Soft Film Forming Acrylic Emulsion For Printing Ink

Ask Lasest Price
Brand Name :	WeiLi Resin®
Model Number :	WQ-2015
Certification :	ISO9001
Price :	Negotiable
Payment Terms :	L/C, T/T
Supply Ability :	500t/month
Delivery Time :	14 work days

Add to Cart

Product Details
Company Profile

Water And Rub Resistance Soft Film Forming Acrylic Emulsion For Printing Ink

Chinese Good Water And Rub Resistance Soft Film Forming Acrylic Emulsion For Printing Ink

Introduction

WQ-2015 acrylic emulsion is recommended for water-based flexographic and gravure inks on flexible films and foils, like PE. It is a film forming emulsion that has good adhesion to various polyolefin films. WQ-2015 acrylic emulsion has excellent water and rub resistance and film wetting and good ddhesion to lots of substrates. It is specially designed for flexo & gravure plastic inks and overprint varnishes. It promotes gloss, holdout, and resolubility in printing ink and overprint varnish formulations and can also be used to produce inorganic and organic pigment dispersion.

It is recommended to use WQ-2015 water based acrylic emulsion and WQ-2011 non-filming acrylic emulslion for water based flxography plastic varnish. The final inks will have excellent water resistance and rub resistance.

Physical Property:

Appearance	Milky white
Solid Content (%)	49±1
Acid Value	50
Viscosity(mPa*s)	1800-3000
PH(25℃)	8.0-9.0
Tg(℃)	-23
MFFT(℃)	<0

Rerefence Formulation For Water Based Varnish For Plastic Substrate (Flexography)

No.	Raw Materials	%
①	WQ-2015 (soft film-forming)	70.00
②	WQ-2011 (hard-film forming)	19.00
③	WQ-2028 (improving gloss)	5.50
④	Wax emulsion	4.00
⑤	DOWSIL™ 51 : Ethanol (1:1) *	1.00	Dow Corning
⑥	Defoamer	0.50	TEGO Foamex 825
Total		100.00
Remark: 1. ①＋②＋③+④+⑤＋⑥ Add the above materials and stir at the same time, at a constant speed, stirring time: about 30 minutes/300 rpm. 2. *: DOWSIL™ 51 Additive diluted with Ethanol =1:1 3. 4# cup: 25 seconds ± 2 PH value: 8.20 ± 0.5% 4. Final inks: varnish 70%+pigment paste 30% =100 (Ajusting it accoring to needs)

Performance:

Self-closslinking and Excellent film-forming
Water-based flexographic and gravure inks on flexible films substrate
High adhesion force
High resistance to water, Oil.
High friction coefficient

Water And Rub Resistance Soft Film Forming Acrylic Emulsion For Printing Ink
Packing
1000kg/IBC
200kg small mouth plastic drum

Product Tags:


*From:	Your email address is incorrect!
*To:	Xiamen WangQin Chemical Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!